The present work investigates γ-channel dislocation reactions. which govern low-temperature (T = 750 °C) and high-stress (resolved shear stress: 300 MPa) creep of Ni-base single crystal superalloys (SX). It is well known that two dislocation families with different b-vectors are required to form planar faults. which can shear the ordered γ’-phase. https://www.ealisboa.com/top-offer-Telemarkskongen-SH-best-find/